Glaxs is a high adhesion system for indoor and outdoor bonding of ceramic, porcelain, and similar surfaces.
Available in a wide variety of colors. Requires use of special M200XMR Cartridge Gun.
GLAXS ADVANTAGES:
- VOC free
- Excellent adhesion
- Ultra rapid
- Excellent color stability to sunlight
- Glossy, shiny and easy to polish
- Indoor and Outdoor use
- Pre-dosed for easy dispensing
- Comes with 2 mixing nozzles
GLAXS CLEAN WHITE INSTRUCTIONS FOR USE:
- All the surfaces to be treated must be cleaned and free of dust and grease.
- In case of glossy and/or smooth surfaces, we suggest to scrub the surfaces with sandpaper before gluing.
- Remove the threaded extremity and uncap the cartridge.
- Fix the mixer to the cartridge through the threaded nozzle.
- Before applying the glue on the surfaces, do spurge around 5 gr in line.
- Use only guns approved by Tenax, MK Sulzer ratio 2+1 H236M and Mixpac DM200-01 ratio 2+1.
- After usage, clean the nozzle, replace the cap and discard the mixer after use. Product will not set below +1°C.
SHELF LIFE:
Glaxs Clean White in cartridge will last at least 12 months, in normal conditions between 18-25°c, kept away from source of heat, humidity and sun light.
SAFETY RULES:
Resin and hardener are chemical products, please read the safety data sheet before usage and the rules written on the product label.
- Gel time in bulk at 77°: 3-5 min
- Tacky free time at 77°: approx. 15 min
- Working time at 77°: 45-60 min
- Temp range for use after hardening: -13°F to 140°F
| Viscosity cps 25°C 20 r.p.m (ASTM D2196) | tixotropic liquid |
| Density at 25°C gr/cm3 | 1.27 |
| Aspect | colored liquid |
| Ratio of use glue/hardener | 2+1 |
| Gel time (in bulk) at 25°C in min | 3-5 min |
| Time for handling pieces | 15-20 min |
| Working time suggested at 25°C in min | 45-60 min |
| Minimum reaction temperature | +1°C |
| Minimum temperature of use after hardening | -25°C |
| Minimum temperature of use after hardening | +60°C |
| Shelf life at 18-20°C | 24 months |
| Adhesion force in MPa at 25°C on natural stone, diamond cut surface after 1 hour (ASTM D 4541)* | 9.0 - 10.0 |
| Adhesion force in MPa at 25°C on natural stone, diamond cut surface after 24 hours (ASTM D 4541)* | 9.5 - 10.5 |
| Adhesion force in MPa at 25°C on quartz, diamond cut surface after 1 hour (ASTM D 4541)* | 9.0 - 10.0 |
| Adhesion force in MPa at 25°C on quartz, diamond cut surface after 24 hours (ASTM D 4541)* | 12.0 - 13.0 |
| Adhesion force in MPa at 25°C on ceramic, diamond cut surface after 1 hour (ASTM D 4541)* | 9.0 - 11.0 |
| Adhesion force in MPa at 25°C on ceramic, diamond cut surface after 24 hours (ASTM D 4541)* | 10.0 - 13.0 |